Pan Fiber Roving

Model NO.: XG-1K
Width: 1mm
Function: High Strength Fiber
Structure: Synthetic Carbon Chain
Model: Xg-1k
Filament Number: 1k
Linear Density: 120tex
Linear Density of Monofilament: 0.122+/-0.003tex
Linear Density Deviation From Nominal: Max.+/-5%
Tensile Strenght for Single Fiber: Min.58 Cn/Tex
Elongation at Break: 12+/-3%
Oil Content: 1.2+/-0.5%
Humidity: <0.1%
Trademark: XIANGU
Transport Package: Cartons
Specification: ROHS
Origin: Guangdong
HS Code: 5503300000
Model NO.: XG-1K
Width: 1mm
Function: High Strength Fiber
Structure: Synthetic Carbon Chain
Model: Xg-1k
Filament Number: 1k
Linear Density: 120tex
Linear Density of Monofilament: 0.122+/-0.003tex
Linear Density Deviation From Nominal: Max.+/-5%
Tensile Strenght for Single Fiber: Min.58 Cn/Tex
Elongation at Break: 12+/-3%
Oil Content: 1.2+/-0.5%
Humidity: <0.1%
Trademark: XIANGU
Transport Package: Cartons
Specification: ROHS
Origin: Guangdong
HS Code: 5503300000
PAN fiber roving/Polyacrylonitrile precursor is high purity and high strength fiber through wet-two step method with solvent DMF and surface finishing size treatment.It has higher elastic modulus,tensile strength and anti-UV properties,anti-high temperature and cold performance.It is the best raw material of PAN carbon fiber Via Pre-oxidation(200~300ºC),carbonization(1000~1500ºC), Graphitization(2500~3000ºC).

SPECIFICATIONS:
MODEL XG-1K
FILAMENT NUMBER 1K
LINEAR DENSITY 120tex
LINEAR DENSITY
OF MONOFILAMENT		 0.122
±0.003tex
LINEAR DENSITY
DEVIATION FROM NOMINAL		 Max.±5%
TENSILE STRENGHT
FOR SINGLE FIBER		 Min.58 cN/tex
ELONGATION AT BREAK 12±3%
OIL CONTENT 1.2±0.5%
HUMIDITY ≤0.1%


APPLICATION FIELDS:
carbon fiber roving productions or carbon fiber filament manufacturing.
STORAGE:
The polyacrylonitrile precursor should be keep dry in their original cartons and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire

PACKAGING:
1.Inner paper pipe bobbin,net weight 6.00kg.gross weight 7.00kg
2.Carton size:600mm*360mm*190mm,net weight 36.00kg.gross weight 43.00kg.


SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 648 cartons one 20feet container,total net weight is 23328.00kg.
2.transportation by truck:for truck transportation,generally loading in buck with 6layers,about 11664.00kg
3.transportation by rail:for rail transportation,generally loading in buck,about 57600.00kg.   PAN fiber roving/Polyacrylonitrile precursor is high purity and high strength fiber through wet-two step method with solvent DMF and surface finishing size treatment.It has higher elastic modulus,tensile strength and anti-UV properties,anti-high temperature and cold performance.It is the best raw material of PAN carbon fiber Via Pre-oxidation(200~300ºC),carbonization(1000~1500ºC), Graphitization(2500~3000ºC).

SPECIFICATIONS:
MODEL XG-1K
FILAMENT NUMBER 1K
LINEAR DENSITY 120tex
LINEAR DENSITY
OF MONOFILAMENT		 0.122
±0.003tex
LINEAR DENSITY
DEVIATION FROM NOMINAL		 Max.±5%
TENSILE STRENGHT
FOR SINGLE FIBER		 Min.58 cN/tex
ELONGATION AT BREAK 12±3%
OIL CONTENT 1.2±0.5%
HUMIDITY ≤0.1%


APPLICATION FIELDS:
carbon fiber roving productions or carbon fiber filament manufacturing.
STORAGE:
The polyacrylonitrile precursor should be keep dry in their original cartons and stored in a suitable place,preferably at room temperature with 35-65% relative humidity.Avoid the sun, rain and fire

PACKAGING:
1.Inner paper pipe bobbin,net weight 6.00kg.gross weight 7.00kg
2.Carton size:600mm*360mm*190mm,net weight 36.00kg.gross weight 43.00kg.


SHIPMENT AND TRANSPORTATION:
1.Shipment by sea:for sea transportation,generally 648 cartons one 20feet container,total net weight is 23328.00kg.
2.transportation by truck:for truck transportation,generally loading in buck with 6layers,about 11664.00kg
3.transportation by rail:for rail transportation,generally loading in buck,about 57600.00kg. Â